Pigmented resin. Ideal as a finishing coating for smooth systems

Pigmented, two-component, solvent free, casting epoxy, low-viscosity resin. Ideal as a finishing coating for smooth systems.

Product data sheet SICONOFLOOR SL100-E



Physical properties of Siconofloor SL100-E
Form Component A modified colorful epoxy liquid
Component B amine curing agent
Density (according to PN EN ISO 1675) Component A 1.1~1.2 g/cm
Component B 0.89~1.05 g/cm3
Suitability for use 40 minutes at 20oC
Theoretical consumption of the blend Minimum 2.0 kg/m2 in case of using as a self-leveling compound
Color and odor Component A colorful and odorless
Component B transparent, with a characteristic odor
Hygiene tests Meets the requirements; Hygienic Certificate No. HK/B/0757/01/2015
Curing time Light load 24h at 25oC
Full load 7 days
Viscosity (Brookfield DV-II). The test was conducted at 19oC using 04 spindle and rotational speed. 20 RPM. Component A 1150~1250 mPa*s
Component B 710~780mPa*s

Mechanical properties of Siconofloor SL100-E
Dust dryness 12 hours at 20oC
ShA hardness (after 7 days) 100o
ShA hardness (after 7 days) 80o

Application methods First mix A component (3 minutes), then add B component, mix the components until a uniform consistency, but not for less than 3 minutes. Stirring ratios of Component A and Component B are indicated on the packaging and they must not be changed. Changing the proportions results in a product with characteristics different from the ones declared by the manufacturer. Over mixing can cause air entrainment and therefore it should be avoided. Use low speed electric stirrer for the resin mixing (300 ÷ 400 rpm) or another suitable equipment.
Casting coating – smooth system Apply SICONOFLOOR SL100-E using a metal trowel equipped with a suitable detachment to regulate efficiency according to the art of painting, ensure that a uniform and continuous coating is obtained. The material must be bleed with a spiked roller.
Conditions of the system components storage SICONOFLOOR SL100-E resin is a material with a reduced tendency to crystallization process. Store it in a dry place at 5~30oC. Components A an B in a liquid state are the agents causing water pollution and should not get into drains, soil and watercourses. After curing the resin is environmentally neutral.

Sicon Spółka z ograniczoną odpowiedzialnością Sp. k.

Pod Borem 22B, 36-060 Głogów Małopolski near of Rzeszow

NIP: 517 02 71 717 REGON: 180372420 KRS: 0000633637
Sąd Rejonowy w Rzeszowie XII Wydział Gospodarczy Krajowego Rejestru Sądowego