Colorless resin. Ideal for “Stone Carpet” type systems

Colorless, two-component, solvent free, epoxy, low-viscosity resin. Ideal for “Stone Carpet” type systems as structural and sealing coating.

Product data sheet SICONOFLOOR CS-E



Physical properties of Siconofloor CS-E
Form Component A modified epoxy liquid
Component B amine curing agent
Density (according to PN EN ISO 1675) Component A 1.05~1.2 g/cm3
Component B 0.99~1.15 g/cm3
Suitability for use 3 hours at 20oC
Color and odor Component A transparent and odorless
Component B liquid with a characteristic odor
Hygiene tests Meets the requirements; Hygienic Certificate No. HK/B/0757/01/2015
Curing time Light load after 72h at 25oC:
Full load 10 days
Practical use of the blend It strongly depends on the use, aggregate fractions, application technique, application conditions, roughness degree: see the system data sheet
Viscosity (Brookfield DV-II). The test was conducted at 20oC using 04 spindle and rotational speed. 20 RPM. Component A 1090~1100 mPa*s
Component B 700~732 mPa*s
Stirring ratio A:B 100:26 (by weight)

Mechanical properties of Siconofloor CS-E
Dust dryness 72 hours at 20oC
ShA hardness (after 10 days) 100o
ShD hardness 83o

Application methods First mix A component, then add B component, mix the components until a uniform consistency, but not for less than 3 minutes. Quartz sand may be added to the mixed A and B components, if required, mix for other 2 minutes until a homogeneous blend. Stirring ratios of Component A and Component B are indicated on the packaging and they must not be changed. Changing the proportions results in a product with characteristics different from the ones declared by the manufacturer. Over string can cause air entrainment and therefore it should be avoided. Use low speed electric stirrer for the resin mixing (300 ÷ 400 rpm) or another suitable equipment.
Resin screed Spread SICONOFLOOR CS-E along with appropriate aggregate using battens of steel, best on guide rails. After a short time, the mortar must be compacted and leveled with fingers or a mechanical float (20-90 rpm) with blades coated with chemical resistant material. The proportions of SICONOFLOOR CS-E resin to the aggregate depends on the aggregate grain size, but the most commonly 8% of resin weight of the aggregate is used. Wash tools with acetone or xylene immediately after use. Hardened or cured material can only be removed mechanically.
Conditions of the system components storage SICONOFLOOR B50-E resin is a material with a reduced tendency to crystallization process. Store it in a dry place at +5~30oC. Components A an B in a liquid state are the agents causing water pollution and should not get into drains, soil and watercourses. After curing the resin is environmentally neutral.

Sicon Spółka z ograniczoną odpowiedzialnością Sp. k.

Pod Borem 22B, 36-060 Głogów Małopolski near of Rzeszow

NIP: 517 02 71 717 REGON: 180372420 KRS: 0000633637
Sąd Rejonowy w Rzeszowie XII Wydział Gospodarczy Krajowego Rejestru Sądowego